PAHT CF 9891 BK powered by LUVOCOM® 3F
NEEMA3D PAHT CF 9891 BK powered by LUVOCOM® 3F is a 15% carbon fiber reinforced material. Suitable for industrial applications, easy to print with low warping an increased layer adhesion. If you are looking for a PA6 based material with low influence from moisture and temperature and dimensional stability with electrical properties then this filament is your choice!
- Carbon Fiber Reinforced Material (15%)
- Extremely stiff
- Designed for industrial applications
- PA6 based material
- Low warping and increased layer adhesion
Specifications
Dimensions
| Size | ø tolerance | Roundness |
|---|---|---|
| 1,75mm | ø 0,05mm | 95% |
| 2,85mm | ø 0,10mm | 95% |
Physical properties
| Description | Testmethod | Typical value |
|---|---|---|
| Specific gravity | ISO 1183 | 1,24 g/cc |
| MFI 250c/2,16Kg | ISO 1183 | 4 g/10 min |
| Tensile strength at yield | ISO 527 | 120 MPa |
| Elongation strain at yield | ISO 527 |
2% |
| Tensile modulus | ISO 527 | 10500MPa |
| Water absorption 23°C | ISO 62 | <0,3% |
| Mold shrinkage | DIN 16742 | 0,3-0,5% |
| Impact strength - Charpy noteched 23c | ISO 179 | 35 kJ/m² |
Thermal properties
| Description | Testmethod | Typical value |
|---|---|---|
| Printing temp. | - |
260±5˚C |