PAHT 9936 BK powered by LUVOCOM® 3F
NEEMA3D PAHT 9936 BK powered by LUVOCOM® 3F is an unreinforced polyamide-based filament. This filament has excellent tensile and impact strength and allows continued operation up to 100°C – 120°C while retaining 50% of its mechanical properties and short-term 160°C.
- Unreinforced PAHT
- Optimized surface appearance
- Designed for industrial applications
- PA6 based material
- Low warping and increased layer adhesion
Specifications
Dimensions
| Size | ø tolerance | Roundness |
|---|---|---|
| 1,75mm | ø 0,05mm | 95% |
| 2,85mm | ø 0,10mm | 95% |
Physical properties
| Description | Testmethod | Typical value |
|---|---|---|
| Specific gravity | ISO 1183 | 1,25 g/cc |
| MFI 250c/2,16Kg | ISO 1183 | 6 g/10 min |
| Tensile strength at yield | ISO 527 | 78 MPa |
| Elongation strain at yield | ISO 527 |
4,4% |
| Tensile modulus | ISO 527 | 3400MPa |
| Water absorption 23°C | ISO 62 | <0,3% |
| Mold shrinkage | DIN 16742 | 0,3-0,5% |
| Flexural modulus | ISO 178 | 6000 MPa |
| Flexural strength | ISO 178 | 78 MPa |
| Vicat softening temp. A | ISO 306 | 80°C |
| Heat deflection temp. A (1,8MPa) | ISO 75 | 90°C |
Thermal properties
| Description | Testmethod | Typical value |
|---|---|---|
| Printing temp. | - |
265±5˚C |